研究了表面改性对活性炭吸附苯酚性能的影响。研究发现,硫酸氧化可增加活性炭表面酸性基团的含量,提高了活性炭的表面亲水性,降低pHPZC值,因而对吸附水中的苯酚的性能产生明显影响,降低了对苯酚的吸附。     

Effects of the sintering atmosphere on Nb-based dielectrics

The effects of a forming atmosphere on the stability, the sintering and the dielectric properties of Ba₅Nb₄O₁₅, BaNb₂O₆, ZnNb₂O₆ and Zn₃Nb₂O₈ ceramics were investigated, because of the primary importance of the sintering atmosphere in relation to copper sintering. These Nb-based materials were sintered in air and in Ar/H₂10%. Zn-containing samples are very sensitive to the reductive atmosphere. ZnO volatilises at 800–850 °C and the resulting compound does not exhibit the expected properties. BaNb₂O₆ and Ba₅Nb₄O₁₅ are more stable in term of relative weight loss. Nevertheless, the phase analysis reveals a modification of the BaNb₂O₆ phase, what induces the degradation of the dielectric property stability versus temperature. The properties of Ba₅Nb₄O₁₅ are not modified by a sintering in reductive atmosphere. A relative permittivity of 38.8, a permittivity temperature coefficient of −150 ppm °C⁻¹ and an insulating resistivity of 10^10.9 Ω cm were obtained for this latter.     

Compatibility of polysaccharide/maleic copolymer blends. IV. Thermal behavior of hydroxypropyl cellulose‐containing blends

The compatibility of the hydroxypropyl cellulose (HPC) with maleic acid–vinyl acetate copolymer in the solid state was studied by thermogravimetry, thermo‐optical analysis, differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FTIR), and optical microscopy. It was established that physical interactions are prevalent in blends with a high content of HPC, whereas chemical interactions predominate in blends with a medium and low content of HPC. By increasing the temperature, the thermochemical reactions are favored. Thermal properties are dependent on the mixing ratio of the components. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 2585–2597, 2003     

Application of statistical mechanics to the analysis of various physical properties of elastomeric networks — a review

This paper examines the application of the statistical mechanics to the analysis of various physical properties of the elastomeric networks. The equilibrium properties of rubber-like networks are discussed, and also some dynamic properties, such as the relaxation spectrum of Gaussian networks. The paper covers a large spectrum of properties of polymer networks such as: fluctuations and chain dimensions in unimodal and bimodal network, effects of entanglements and constraints on the elastic properties of the network, segmental orientation, liquid-crystalline networks, small angle neutron scattering from networks, strain birefringence, elastic properties of filled networks, strain induced crystallization etc. The paper shows that the statistical mechanics can be successfully used to the analysis of almost all physical properties of rubber-like networks.     

Exploring the effect of dry premixing of sand and cement on the mechanical properties of mortar

A spout-fluid bed device was developed for dry premixing sand and cement to produce mortar. The goal of the work was to explore the efficacy of a new method for dispersing cement in sand to produce a mortar with better mechanical and physical properties. This strategy was found to work best at high sand/cement ratios, indicating that the dry premixing is more effective as the cement content is reduced and that it may be possible to produce commercially acceptable mortars with a lower cement content. Other properties of the mortar are also positively affected, including a decrease in the shrinkage and an increase in the workability.     

硅/碳化硅材料显微特征与强度关系研究

通过改变坯体碳/碳化硅质量比,采用反应烧结方法制备了不同硅相含量和次生碳化硅分布形式的硅/碳化硅复合材料。探讨了该复合材料不同显微组织的形成机理。用三点弯曲法评价了材料强度与显微组织的关系,结合断口断裂模式,从热失配引起颗粒周围残余应力和界面能两个方面对强度-组织之间的关系进行了定性讨论。结果表明,硅/碳化硅相体积含量、碳化硅分布形态、热失配导致的残余应力是影响材料强度的主要因素,优化制备工艺参数是获得高性能材料的关键。     

Molecular design and characterization of catalysts for NO x selective reduction by hydrocarbons in the oxygen excess based upon ultramicroporous zirconia pillared clays

Approaches to design of zirconia pillared clays via control of the properties of pillaring species in solutions were elaborated. Structural features of pillars and Pt + Cu active components fixed at these nanoparticles were shown to determine catalytic properties of pillared clays in NO_x selective reduction by hydrocarbons in the oxygen excess.     

Modeling the large‐strain constitutive behavior of polycarbonate under isothermal and anisothermal conditions

The tensile behavior of polycarbonate was studied at large strains below the glass‐transition temperature. Experiments were carried out at a series of constant temperatures and also under conditions of falling temperatures. The specimens necked with a natural draw ratio of approximately 2, and the study was mainly focused on the necked material. Isothermal experiments revealed an elastic mechanism that initiated beyond the natural draw ratio. A model consisting of an Eyring process and two Gaussian elastic mechanisms was found to be applicable to both the isothermal and anisothermal stress‐relaxation and stress–strain results. The same model also produced reasonable estimates of the stresses generated during the necking process. In addition, a simple relationship between the isothermal and anisothermal stress relaxation was demonstrated. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 96: 2105–2116, 2005     

Modification of the polarity of isotactic polypropylene through blending with oxidized paraffin wax

The modification of the polarity of isotactic polypropylene (iPP) through blending with oxidized paraffin wax (Fischer–Tropsch synthesis) was investigated. The oxidized paraffin wax significantly increased the polar component of the total surface free energy of polypropylene. Modified iPP also showed significantly higher adhesion to the polar substrate, as represented by a crosslinked epoxy‐based resin. The conservation of the good mechanical properties of the blends was observed up to 6 wt % wax. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 94: 529–533, 2004     

二种双邻位甲基取代的聚芳醚酮类树脂的合成与性能

合成二种双邻位甲基取代的聚芳醚酮类聚合物,聚芳醚酮醚酮酮(DM-PEKEKK)和聚芳醚酮酮醚酮酮(DM-PEKKEKK),用FT-IR、1H NMR、DSC、WAXD、TG等技术对其进行表征,研究表明:较之于未取代的PEKEKK和PEKKEKK玻璃化转变温度和溶解性能大幅度提高,热分解温度有所下降,但均在450℃以上.